Study Effect Treatment Thermal for Cermet Composite Prepared by Flame Thermal Spray Method. | |||||||||||
Kirkuk University Journal-Scientific Studies | |||||||||||
Article 3, Volume 15, Issue 4, Autumn 2020, Page 42-55 PDF (1518 K) | |||||||||||
Document Type: Research Paper | |||||||||||
DOI: 10.32894/kujss.2021.167517 | |||||||||||
Author | |||||||||||
S. H. Hameedi ![]() | |||||||||||
Department of Physics, College of Science, University of Tikrit, Tikrit, Iraq. | |||||||||||
Abstract | |||||||||||
Flame thermal spraying technology was used in the production of 25% zirconia composite material with 25% alumina particle with binder material of 50% Al-Ni alloy base on 316L alloy steel base, after preparation the base surface with a method of roughing the granular. Spraying was carried out using a spray distance (12,14,16,18,20) cm. Hardness tests were carried out on the composite material to study the effect of changing spray distance on the properties of the resulting layer. The thermal treatment was performed on the samples at (850,950,1050,1150) for an hour. The results of the tests confirmed that the best spraying distance (16 cm) and the thermal treatment (1050 ) have a significant effect on improving the hardness of the layers of the composite material. | |||||||||||
Keywords | |||||||||||
Composite Materials; Material Engineering; Spray Techniques | |||||||||||